广东工业大学学报 ›› 2018, Vol. 35 ›› Issue (02): 6-10.doi: 10.12052/gdutxb.170148

• • 上一篇    下一篇

无纺布负载锰氧化物的制备及其催化分解甲醛性能研究

周祖卫1, 余倩1, 郝志峰1, 张佐宏2, 罗银好2, 余林1, 戴立松3   

  1. 1. 广东工业大学 轻工化工学院, 广东 广州 510006;
    2. 佛山沛涂科技有限公司, 广东 佛山 528200;
    3. 表面测量仪器公司 中国办事处, 北京 101300
  • 收稿日期:2017-11-02 出版日期:2018-03-09 发布日期:2018-03-13
  • 通信作者: 余倩(1964-),女,教授,博士,主要研究方向为环境催化.E-mail:yuqgdut@126.com E-mail:yuqgdut@126.com
  • 作者简介:周祖卫(1992-),男,硕士研究生,主要研究方向为环境催化.
  • 基金资助:
    国家自然科学基金资助项目（51678160）；广东省科技计划项目（2016A020221033）；广州市科技计划项目（201704020202）；佛山高新区战略性新兴产业发展项目

Preparation of Manganese Oxide Supported on Non-woven Fabric and Its Catalytic Performance for Formaldehyde Decomposition

Zhou Zu-wei1, Yu Qian1, Hao Zhi-feng1, Zhang Zuo-hong2, Luo Yin-hao2, Yu Lin1, Dai Li-song3   

  1. 1. School of Light Industry and Chemical Engineering, Guangdong University of Technology, Guangzhou 510006, China;
    2. Foshan Peico Technology Co., Ltd, Foshan 528200, China;
    3. China Office, Surface Measurement Systems, Beijing 101300, China
  • Received:2017-11-02 Online:2018-03-09 Published:2018-03-13
  • Supported by:
     

HTML

PDF (PC)

2958

摘要： 随着物质生活的不断提高，甲醛成为了室内空气污染的主要物质，对于室内空气净化过程，去除甲醛技术变得尤为重要. 利用条件温和、过程简单的水浴法使二氧化锰（MnO2）原位负载到聚对苯二甲酸乙二醇酯（PET）制成的无纺织物上，制备出MnO2/PET整体式催化剂. 合成的MnO2/PET复合物通过扫描电子显微镜（SEM）、X射线衍射（XRD）、比表面积测试（BET）进行表征分析，并在手套箱中模仿室内环境进行甲醛去除测试以及催化剂寿命测试. 结果表明：整体式催化剂中的锰氧化物为水钠锰矿型二氧化锰，并均匀、牢固负载在无纺布上. 由于其有较大的比表面积，在甲醛去除能力方面展示出了优良的性能，在甲醛初始质量浓度为2.84 mg/m3的氛围测试中经过6 h，最后使甲醛质量浓度降低至0.33 mg/m3，甲醛去除率达到88.29%. 提供了一种高效的去除甲醛的催化剂合成方法，这种整体式催化剂为室内甲醛催化净化拓展了新的思路.

关键词: 无纺布, 二氧化锰, 甲醛, 催化分解, 高效

Abstract: With the continuous improvement of material life, formaldehyde has become the main substance of indoor air pollution. For indoor air purification, the removal of formaldehyde becomes particularly important. Manganese dioxide (MnO2) was in-situ loaded onto non-woven fabric made of polyethylene terephthalate (PET) by water bath method, which has mild reaction conditions and simple processing. The synthesized MnO2/PET composites were characterized by scanning electron microscope (SEM), diffraction of X-rays (XRD) and specific surface area test (BET), imitating the indoor environment to make the initial concentration of 2.84 mg/m3, after 6 h, and making the concentration of the formaldehyde to 0.33 mg/m3, with the removal rate of formaldehyde reaching 88.29%. This study provides an efficient method for the synthesis of formaldehyde oxidation catalyst, which provides a new idea for indoor formaldehyde catalysis.

Key words: non-woven fabric, manganese dioxide, formaldehyde, catalytic oxidation, efficient

中图分类号: 

  • TQ426.64
[1] 杨俊松, 钟颖颖, 余倩. IrO2@MnO2纳米酶的制备及用于抗坏血酸的检测[J]. 广东工业大学学报, 2022, 39(02): 130-136.
[2] 黄涛涛, 刘立程, 彭同壮. 基于运动特性的帧间预测模式快速选择算法[J]. 广东工业大学学报, 2020, 37(02): 74-79.
[3] 符志伟，程高，林婷，孙明，余林. 二氧化锰制备及催化燃烧甲苯性能研究[J]. 广东工业大学学报, 2016, 33(02): 85-90.
[4] 李志生, 郭初. 温湿度对典型家具材料甲醛散发的影响研究[J]. 广东工业大学学报, 2015, 32(2): 132-136.
[5] 张然, 梁亮, 宛焱, 胡龙. 纳米银水性抗菌木器涂料的研制[J]. 广东工业大学学报, 2015, 32(04): 40-45.
[6] 邓淑华； 李期颁； 沈薇； . 苯乙烯改性醇酸树脂涂料相对分子质量及其分布的测定[J]. 广东工业大学学报, 1999, 16(3): 99-101.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 2017 《广东工业大学学报》编辑部
地址：广州市东风东路729号广东工业大学 邮编：510090
电话：020-37626653,020-37626139,020-37626396
邮箱：xbzrb@gdut.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发