高功率脉冲磁控溅射技术沉积硬质涂层研究进展

王启民1，张小波2，张世宏3，王成勇1，伍尚华1   

  1. 1.广东工业大学 先进加工工具与高技术陶瓷研究中心，广东 广州 510006;
    2.深圳速普仪器有限公司，广东 深圳 518054;3 安徽工业大学 材料科学与工程学院，安徽 马鞍山 243011
  • 收稿日期:2013-11-18 出版日期:2013-12-30 发布日期:2013-12-30
  • 作者简介:王启民（1977-），男，教授，博士生导师，中组部“青年千人计划”入选者，广东省高校“珠江学者”特聘教授，德国洪堡学者,主要研究方向为刀具、模具用硬质涂层和汽车、航空热端部件高温防护涂层.
  • 基金资助:

    国家自然科学基金资助项目（51275095、U1201245）；珠江科技新星项目（2011J2200036）；广东省高等学校珠江学者岗位计划资助项目（2012）

Progress of High Power Impulse Magnetron Sputtering for Deposition of Hard Coatings

Wang Qi-min1， Zhang Xiao-bo2， Zhang Shi-hong3，Wang Cheng-yong1，Wu Shang-hua1   

  1. 1.Advanced Cutting Tools and Ceramics Center, Guangdong University of Technology, Guangzhou 510006, China;
    2.Shenzhen SuPro Instruments Company Limitied，Shenzhen 518054, China;
    3.School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan 243011, China
  • Received:2013-11-18 Online:2013-12-30 Published:2013-12-30

HTML

PDF (PC)

3579

摘要： 高功率脉冲磁控溅射技术是最新发展起来并受到广泛关注的一种高离化率物理气相沉积技术，它利用较高的脉冲峰值功率（超出传统磁控溅射2~3个数量级）和较低的脉冲占空比（0.5%~10%）来实现高金属离化率（>50%），在获得优异的膜基结合力、控制涂层微结构、降低涂层内应力、控制涂层相结构等方面都具有显著的技术优势.本文从高功率脉冲磁控溅射技术的原理出发，探讨了高功率脉冲溅射技术沉积涂层的特性和技术优势，介绍了10多年来高功率脉冲磁控溅射技术在刀具涂层界面优化、高性能硬质涂层沉积、复合高功率脉冲磁控溅射技术制备纳米多层/复合硬质涂层和氧化物涂层沉积、低温沉积等方面的研究进展.

关键词: 高功率脉冲磁控溅射技术；离化率；硬质涂层；反应溅射

Abstract: High power impulse magnetron sputtering (HIPIMS) is an emerging highionization physical vapor deposition technology which was has gained substantial interests. It utilizes pulses of high peak power density (2-3 orders higher than the conventional magnetron sputtering) and low duty cycle (0.5%-10%) leading to high ionization of metal atoms. This mode has distinguished advantages during deposition:  high adhesive strength, controllable microstructure and phase structure, and decreased residual stress, etc. This review covers the basic principle of HIPIMS, the characteristic of films & coatings deposited by HIPIMS, and the developments of HIPIMS technologies in the recent 10 years: optimization of coatingsubstrate interface in the coated cutting tools, deposition of highperformance hard coatings, nanolayered/nanocomposite coatings by hybrid HIPIMS, oxide coatings, lowtemperature coatings, etc. 

Key words: high power impulse magnetron sputtering; ionization ratio; hard coating; reactive sputtering

No related articles found!
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 2017 《广东工业大学学报》编辑部
地址：广州市东风东路729号广东工业大学 邮编：510090
电话：020-37626653,020-37626139,020-37626396
邮箱：xbzrb@gdut.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发