Synthesis of Sr2-M gx Si2 O7：Eu ，Dy’ and Their Luminescent Properties

  

  1. Facudy of Physics and Optoelectronic Engineering，Guangdong University of Technology，Guangzhou 510006，China
  • Online:2010-03-25 Published:2010-03-25

HTML

PDF (PC)

2436

Abstract: The long afterglow luminescent materials Sr2一Mg Si2O7：Eu“，Dy¨( =1．4，1．2，1，0．8，0．6)were synthesized by high temperature solid-state reaction．According to the X—ray diffraction analysis，it was found that the phase of the materials was Sr2MgSi2O7 when the ≥ 1．Three phases have been found when the <1．When ≥1，with the decrease of ，the blHe shift of the emission peak appears through the ph0toluminescence．The depths of the traps were analyzed through the afterglow CHIVES and the thermolumineseence spectra．With the decrease of ，the decay time of the samples decreases，and the traps of the phosphors become shallow．

Key words: long afterglow；silicate；rare earth；trap

[1]柳成，王银海，陈仁，等．sr ca。一 A1 O ：Eu“ ，Dy“ 长余辉发光材料的合成与光学性能研究[J]．功能材料，2007，38(增刊)：124—127．

[2]王晓欣，林元华，张中太．Eu，Dy共添加的Sr2MgSi：O 基长余辉发光材料[J]．硅酸盐学报，2002，30(2)：216-219．

[3]姜伟棣．长余辉发光材料的研究进展[J]．材料导报，2007，21(8)：106—110．

[4]毛大立，赵莉，常程康，等．纳米Sr MgSi O ：Eu“ ，Dy“的长余辉发光行为[J]．无机材料学报，2005，20(1)：220．224．

[5]姜洪义，徐博．高温固相法制备硅酸盐长余辉发光材料[J]．硅酸盐学报，2006，34(9)：1154—1157．

[6]齐晓霞，赵军武，冯异．长余辉材料Sr MgSi：O ：Eu“ ，Dy”的制备及发光性能研究[J]．中国稀土学报，2006，24(增刊)：69-73．

[7]Geng X，Chen Y，Qiu G，et a1．Synthesis of long afterglow photoluminescent materials Sr2 MgSi2 O7：Eu ，Dy by solgel method[J]．Journal of rare earth，2005，23(3)：292—295．

[8]李东平，缪春燕，刘丽芳，等．燃烧法合成新型蓝色硅酸盐长余辉材料及其发光性能的研究[J]．稀有金属，2O04，28(4)：662-665．

[9]姜洪义，姬同坤，李家亮．B掺杂Sr2MgSi 0，电子结构的理论计算[J]．武汉理工大学学报，2008，30(9)：5—8．

[10]Hao J，Gao J，Cocivera M．Tuning of the blue emission from europium—doped alkaline earth chloroborate thin films activated in air[J]．Appl Phys Lett，2003，82(17)：2278—

2280．

[11]Chen R，Wang Y，Hu Y，et a1．Modification Oil luminescent properties of Sr2A1204：Eu ，Dy phospho~ by Ybions doping[J]．J Lumin，2008，128：1 180—1 184．

[12]Liu C，Wang Y，Hu Y，et a1．Adjusting luminescence properties of SrxCa1一 A1204：Eu ，Dy phosphors by Sr／Ca ratio[J]．J Alloy Compd，2009，470：473_476．

[13]张瑞军，张玉奇，刘小蕊，等．稀土蓝色长余辉发光材料的研究进展[J]．中国陶瓷工业，2006，13(4)：37—39．

[14]Fei Q，Chang C，Mao D．Luminescent properties of Sr2MgSi207 and Ca2MgSi207 long lasting phosphom activated by Eu ，Dy [J]．J Alloy Compd，2005，390：133—137．

[15]Kuang J，Liu Y，Zhang J，et a1．Blue—emitting long—lasting phosphor，Sr3A1l0SiO20：Eu“，Ho [J]．Solid State Comnun，2005，136：6—10．

[1 6]Katsumata T，Toyomane S，Tonegawa A，et a1．Characterization of trap levels in longduration phosphor crystals[J]．J Cryst Growth，2002，237—239：361—366．

[17]Matsuzawa T，Aoki Y，Takeuehi N，et a1．A new long phosphorscent phosphors with high brightness，SrAI2 O4：Eu“ ，Dy“[J]．J Electrochem Soc，1996，143(8)：2670-2673．

[18]符义兵，张国斌，戚泽明，等．蓝色长余辉材料Sr2MgSi O ：Eu“，Dy“及其基质的VUV—uV激发特性[J]．发光学报，2006，27(3)：320—324．

[19j Zhang G B，Qi z M，Zhou H J，et a1．Photoluminescence of(Eu Dy ) co—doped silicate long lasting phosphors[J]．J Electron Spectrosc，2005，144—147：861—863．

[20]Aitasalo T，H01sa J，Jungner J，et a1．Thermoluminescence Studv of Persistent Luminescence Materials：Eu2十 andR 一Doped Calcium Aluminates，CaM 2 04：Eu2， R[J]．J Phys Chem B，2006，110：4589-4598．

[21]Lin Y，Tang Z，Zhang Z，et a1．Anomalous luminescence in sr4AIl4O ：Eu，Dy phosphors[J]．Appl Phys Len，2002，81：996—998．
 
No related articles found!
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © 2017 Journal of Guangdong University of Technology
Add：729 East Dongfeng RD., Guangzhou PRC. Postcode: 510090
Tel：020-37626653,020-37626139,020-37626396
Email：xbzrb@gdut.edu.cn
Supported:Beijing Magtech