The Efects of Polarization Potential on Stress Corrosion Cracking(SCC) Behavior of Aluminum Alloy 5083

  

  1. 1．Faculty of Materials and Energy，Guangdong University of Technology，Guangzhou 5 10006，China；
    2．Guangdong Xingfa Aluminum Co．Ltd．，Foshan 528061，China
  • Online:2010-06-25 Published:2010-06-25

HTML

PDF (PC)

2399

Abstract: The effects of polarization potential on stress corrosion cracking(SCC)behavior of 5083 aluminum alloy are investigated by using slow strain rate tension(SSRT)test，SEM，and EDS．The experimental results reveal that under cathodic polarization the values of SCC susceptibility(Issrt)are minimum，the susceptibility is the weakest，and the fracture is a quasi-cleavage one without a few dipples while under anode polarization the values of Issrt are
maximum，the susceptibility is the s~ongest，lots of transverse cracks exist on the fracture surface，and the edges ale corroded．Moreover，the morphology is cleavage-shaped with lots of transgranular and intergranular cracks，belonging to the brittle fracture．SCC behavior of 5083 aluminum is of anodic dissolution．

Key words: 5083 aluminum alloy；polarization potential；SCC susceptibility

[1]刘静安，谢水生．铝合金材料的应用与技术开发[M]．北京：冶金工业出版社，2004．

[2]Parkins R N．Stress Corrosion Cracking-The Slow Strain Rate Technique[M]．Vgiansky：Payer，2006．

[3]王月，吴庭翱．含钪A1-5Mg合金的抗应力腐蚀和剥落腐蚀性能研究[J]．中国腐蚀与防护学报，2005，25(4)：218-221．

[4]罗兵辉，单毅敏，柏振海．退火温度对淬火后冷轧5083铝合金组织及腐蚀性能的影响[J]．中南大学学报：自然科学版，2007，38(5)：802-808．

[5]冷文兵，袁鸽成，倪学明，等．5083铝合金在3．5％NaC1溶液中的应力腐蚀行为[J]．广东工业大学学报，2009，26(1)：65-67．

[6]Song R G，Dietzel W．Stress corrosion cracking and hydrogen embrittlement of an A1-Zn-Mg-Cu alloy[J]．Acta Material，2004，52(16)：4727-4743．

[7]Kiryl A，Yasakaua，Mikhail L，et a1．Role of intermetalic phases in localized corrosion of AA5083[J]．Electrochimica Acta，2007，52：7651-7659．

[8]Jones R H，Vetrano J S，Windisch Jr．Stress corrosion cracking of AI-Mg and Mg·AI alloys[J]．Corosion，2004，60(12)：1144-1154.
No related articles found!
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © 2017 Journal of Guangdong University of Technology
Add：729 East Dongfeng RD., Guangzhou PRC. Postcode: 510090
Tel：020-37626653,020-37626139,020-37626396
Email：xbzrb@gdut.edu.cn
Supported:Beijing Magtech