A Study of Rapid Aging of Automotive Catalyst on the Bench

Zeng En-shan1, Xiong Rui1, Wu Jian1,2, Zhou Xin1, Zhang Zong-lan1   

  1. 1.School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou 510006, China;2.Automotive Engineering Institute, Guangzhou Automobile Group Co. Ltd., Guangzhou 510640, China
  • Received:2016-03-01 Online:2016-11-18 Published:2016-11-18

HTML

PDF (PC)

3431

摘要：

基于车用催化剂的老化机理，建立车用催化剂综合性能试验台架，对催化剂进行160 h的快速老化，比较其老化前后的性能，分析催化剂台架快速老化和实车道路老化的工况法排放结果及相关性.试验结果表明：催化剂经160 h的台架快速老化后，对CO、THC、NOx的起燃温度分别上升了38.5%、28.4%和37.3%；装有160 h台架快速老化后的催化剂相比于装有160 000  km实车老化后的催化剂的整车工况法排放，其THC、CO、NOx和NMHC的排放结果分别增加了8.6%、11.3%、3.8%和13.7%.

关键词: 车用催化剂； 试验台架； 快速老化试验； 数据分析

Abstract:

Based on the aging mechanism of automotive catalyst, a comprehensive performance test bench for automotive catalysts is established to have a 160-hour accelerated aging on the catalyst. The performance of catalyst before and after accelerated aging is compared, and an analysis of correlation and emission by European test cycle for a vehicle after its catalyst being aging on the bench and real vehicle is made. The results show that the light-off temperature of CO, THC, NOx rises by 38.5%, 28.4% and 37.3% respectively after rapid aging of the catalyst on the bench for 160 hours. In addition, compared with the real vehicle catalyst aged after 160 000 km, the emission of THC, CO, NOx, NMHC among the vehicle with the 160 h-rapid aging catalyst on the test bench increases respectively by 8.6%, 11.3%, 3.8% and 13.7%.

Key words: automotive catalyst; test bench; rapid aging test; data analysis

No related articles found!
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 2017 《广东工业大学学报》编辑部
地址：广州市东风东路729号广东工业大学 邮编：510090
电话：020-37626653,020-37626139,020-37626396
邮箱：xbzrb@gdut.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发