广东工业大学学报 ›› 2013, Vol. 30 ›› Issue (3): 118-121.doi: 10.3969/j.issn.1007-7162.2013.03.023

• 综合研究 • 上一篇    下一篇

5083铝合金搅拌摩擦焊焊核区非均匀性组织分析

梁春朗，袁鸽成，吴红辉，吴亚   

  1. 广东工业大学 材料与能源学院，广东 广州 510006
  • 收稿日期:2012-09-05 出版日期:2013-09-30 发布日期:2013-09-30
  • 作者简介:梁春朗（1988-），男，硕士研究生，主要研究方向为先进轻金属材料. 袁鸽成，男，教授，博士，主要研究方向为先进轻金属及微粉材料， E-mail：gchyuan@gdut.edu.cn.
  • 基金资助:

    广东省重大科技专项资助项目（2008A090300004）;广东省教育厅211工程学科建设资助项目(412110903)

Research on Heterogeneity Microstructure of 5083 Aluminum in Nugget Zones after Friction Stir Welding

Liang Chun-lang, Yuan Ge-cheng, Wu Hong-hui, Wu Ya   

  1. School of Materials and Energy, Guangdong University of Technology, Guangzhou 510006, China
  • Received:2012-09-05 Online:2013-09-30 Published:2013-09-30

HTML

PDF (PC)

3266

摘要： 利用小型搅拌摩擦焊机焊接5083铝合金板材，借助电子背散射衍射技术和取向成像分析软件对焊缝焊核区的焊核前进侧、焊核中心区和焊核后退侧的晶粒形貌和取向差角度进行了对比性研究.结果表明：经过搅拌摩擦焊接后，焊核区发生动态再结晶，晶粒由原始带状转变为等轴状，其大角度晶界含量相比于母材有明显增加，但不同部位的晶粒尺寸和大角度晶界比例均不同，焊核前进侧、焊核中心区和焊核后退侧的平均晶粒尺寸分别为17.0、15.8和13.5 μm，大角度晶界比例分别为76.4%、68.8%和73.2%.

关键词: 搅拌摩擦焊；焊核前进侧；焊核中心区；焊核后退侧；微观组织

Abstract: The 5083-H321 aluminum magnesium alloy plates were welded on a minitype friction stir welding machine. The microstructure of friction stir welding (FSW) in each nugget zone was studied via the grain morphology and misorientation distribution of nugget advancing side, nugget median zone and nugget retreating side. The results show that there are small equiaxial grains into which lathshaped grains turn in nugget zones after friction stir welding. However, there are differences in the grain size between the nugget advancing side, nugget median zone and nugget retreating side, and the average grain sides are 17, 15.8 and 13.5 μm, respectively. Compared with the base metal, the high angle grain boundaries(HAGB) fraction in nugget zones increase. Meanwhile the content is also different in the three zones, and they are 76.4%, 68.8% and 73.2%, respectively. 

Key words: friction stir welding; nugget advancing side; nugget median zone; nugget retreating side; microstructure

No related articles found!
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 2017 《广东工业大学学报》编辑部
地址：广州市东风东路729号广东工业大学 邮编：510090
电话：020-37626653,020-37626139,020-37626396
邮箱：xbzrb@gdut.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发