Journal of Guangdong University of Technology ›› 2022, Vol. 39 ›› Issue (01): 34-40,134.doi: 10.12052/gdutxb.210130

Previous Articles     Next Articles

A Study of Preparation and Application Performance of Lignin-based Superhydrophobic Coatings

Liu Xue, Liu Zhong-ming, Xi Yue-bin, Wang Shou-juan, Kong Fan-gong   

  1. State Key Laboratory of Biobased Material and Green Papermaking, Qilu University of Technology (Shandong Academy of Sciences), Jinan 250353, China
  • Received:2021-09-03 Published:2022-01-20

HTML

PDF (PC)

2946

Abstract: Superhydrophobic coatings have drawn much attention in recent years for their wide potential applications. However, a simple and cost-effective approach is still needed for preparing superhydrophobic materials and coatings using natural polymer. Herein, a hierarchical superamphiphobic Lignin-PFTEOS powder was prepared via a substitution reaction. Owing to the substrate-independent characteristics and excellent super-repellency of the powder, it could be applied to various substrates to fabricate superhydrophobic coatings. The prepared coatings have a huge repellency to water, with a water contact angle of 169°, as well as good friction resistance, acid resistance, alkali resistance, salt resistance properties and quite good corrosion resistance performance. After 20 cycles of sand friction or being immersed in 1 mol/L HCl, 0.20 mol/L NaOH and 1 mol/L NaCl solution for 30 minutes, the coatings still retain superhydrophobic capability, with contact angle higher than 150°. Due to its low cost, biodegradability and scalability, lignin-based coatings have huge potential applications in different fields and provide a simple method for the value-added utilization of alkali lignin.

Key words: superhydrophobic, lignin particles, mechanical durability, chemical stability, corrosion resistance

CLC Number: 

  • TQ352.7
[1] XU Q Y, BAI Y Y, ZHAO X, et al. Synthesis and characterization of an amphiphilic lignin-based cationic surfactant [J]. Industrial Crops and Products, 2021, 164: 113376.
[2] YOU X Y, WANG X L, ZHANG H J, et al. Supertough lignin hydrogels with multienergy dissipative structures and ultrahigh antioxidative activities [J]. ACS Applied Materials and Interfaces, 2020, 12(35): 39892-39901.
[3] ZHANG X, LIU W F, CAI J Q, et al. Equip the hydrogel with armor: strong and super tough biomass reinforced hydrogels with excellent conductivity and anti-bacterial performance [J]. Journal of Materials Chemistry A, 2019, 7(47): 26917-26926.
[4] LIU W F, FANG C, CHEN F T, et al. Strong, reusable, and self-healing lignin-containing polyurea adhesives [J]. ChemSusChem, 2020, 13(17): 4691-4701.
[5] MORENO A, MORSALI M, LIU J R, et al. Access to tough and transparent nanocomposites via Pickering emulsion polymerization using biocatalytic hybrid lignin nanoparticles as functional surfactants [J]. Green Chemistry, 2021, 23(8): 3001-3014.
[6] THAKUR V K, THALUR M K, RAGHAVAN P, et al. Progress in green polymer composites from lignin for multifunctional applications: a review [J]. ACS Sustainable Chemistry & Engineering, 2014, 2(5): 1072-1092.
[7] WU B R, CUI X, JIANG H Y, et al. A superhydrophobic coating harvesting mechanical robustness, passive anti-icing and active de-icing performances [J]. Journal of Colloid Interface Science, 2021, 590: 301-310.
[8] ZHANG D J, WU G Q, LI H, et al. Superamphiphobic surfaces with robust self-cleaning, abrasion resistance and anti-corrosion [J]. Chemical Engineering Journal, 2021, 406: 126753.
[9] LIU Z Y, ZHANG C Y, ZHANG X G, et al. Durable superhydrophobic PVDF/FEVE/GO@TiO2 composite coating with excellent anti-scaling and UV resistance properties [J]. Chemical Engineering Journal, 2021, 411: 128632.
[10] XIAO L J, DENG M, ZENG W G, et al. Novel robust superhydrophobic coating with self-cleaning properties in air and oil based on rare earth metal oxide [J]. Industrial & Engineering Chemistry Research, 2017, 56(43): 12354-12361.
[11] PASSAUER L, HALLAS T, BÄUCKER E, et al. Biodegradation of hydrogels from oxyethylated lignins in model soils [J]. ACS Sustainable Chemistry & Engineering, 2015, 3(9): 1955-1964.
[12] GUO J Q, FANG W W, WELLE A, et al. Superhydrophobic and slippery lubricant-infused flexible transparent nanocellulose films by photoinduced thiol-ene functionalization [J]. ACS Applied Materials and Interfaces, 2016, 8(49): 34115-34122.
[13] MONTEIL-RIVERA F, PHUONG M, YE M W, et al. Isolation and characterization of herbaceous lignins for applications in biomaterials [J]. Industrial Crops and Products, 2013, 41: 356-364.
[14] YU M D, MISHRA D, CUI Z Y, et al. Recycling papermill waste lignin into recyclable and flowerlike composites for effective oil/water separation [J]. Composites Part B:Engineering, 2021, 216: 108884.
[15] WANG H, XIONG F Q, TAN Y J, et al. Preparation and formation mechanism of covalent–noncovalent forces stabilizing lignin nanospheres and their application in superhydrophobic and carbon materials [J]. ACS Sustainable Chemistry & Engineering, 2021, 9(10): 3811-3820.
[16] ORIBAYO O, FENG X S, REMPEL G L, et al. Synthesis of lignin-based polyurethane/graphene oxide foam and its application as an absorbent for oil spill clean-ups and recovery [J]. Chemical Engineering Journal, 2017, 323: 191-202.
[17] FENG L, LI S, LI Y, et al. Super-hydrophobic surfaces: from natural to artificial [J]. Advanced materials, 2002, 14(24): 1857-1860.
[18] LI D C, XU W F, CHENG H Y, et al. One-step thermochemical conversion of biomass waste into superhydrophobic carbon material by catalytic pyrolysis [J]. Global Challenges, 2020, 4(4): 1900085.
[19] 张雨晴, 王玺傲, 王兴, 等. 木质素基超疏水涂层的制备与表征[J]. 中国造纸学报, 2019, 34(3): 18-23.
ZHANG Y Q, WANG X A, WANG X, et al. Preparation and characterization of lignin-based superhydrophobic coatings [J]. Transactions of China Pulp and Paper, 2019, 34(3): 18-23.
[20] 顾俐慧. 木质纤维素纳米纤丝基超疏水材料的制备与表征[D]. 南京: 南京林业大学, 2019.
[21] YU C H, WANG F, FU S Y, et al. Laccase-assisted grafting of acrylic acid onto lignin for its recovery from wastewater [J]. Journal of Polymers and the Environment, 2016, 25(4): 1072-1079.
[22] SANTOS R B, CAPANEMA E A, BALAKSHIN M Y, et al. Lignin structural variation in hardwood species [J]. Journal of Agricultural and Food Chemistry, 2012, 60(19): 4923-4930.
[23] HUANG Y X, WANG Z X, HOU D Y, et al. Coaxially electrospun super-amphiphobic silica-based membrane for anti-surfactant-wetting membrane distillation [J]. Journal of Membrane Science, 2017, 531: 122-128.
[24] GUO K, SHARMA A, TOH R J, et al. Porous silicon nanostructures as effective faradaic electrochemical sensing platforms [J]. Advanced Functional Materials, 2019, 29(24): 1809206.
[25] ZHANG Y J, CHEN H L, WANG S J, et al. A new lamellar larch-based carbon material: fabrication, electrochemical characterization and supercapacitor applications [J]. Industrial Crops and Products, 2020, 148: 112306.
[26] ZHANG Y J, CHEN H L, WANG S J, et al. Facile fabrication and structure control of SiO2/carbon via in situ doping from liquefied bio-based sawdust for supercapacitor applications [J]. Industrial Crops and Products, 2020, 151: 112490.
[27] BAHRPAIMA K, FATEHI P. Synthesis and characterization of carboxyethylated lignosulfonate [J]. ChemSusChem, 2018, 11(17): 2967-2980.
[28] ZONG E M, LIU X H, LIU L N, et al. Graft polymerization of acrylic monomers onto lignin with CaCl2–H2O2 as initiator: preparation, mechanism, characterization, and application in poly(lactic acid) [J]. ACS Sustainable Chemistry and Engineering, 2017, 6(1): 337-348.
[29] YE H, ZHU L Q, LI W P, et al. Constructing fluorine-free and cost-effective superhydrophobic surface with normal-alcohol-modified hydrophobic SiO2 nanoparticles [J]. ACS Applied Materials and Interfaces, 2017, 9(1): 858-867.
[1] Zou Shi-xuan，Li Feng，Zhang Ren-yuan. Corrosion of Silicon Carbide and Silicon Nitride in Molten Aluminum Alloy [J]. Journal of Guangdong University of Technology, 2013, 30(1): 106-109.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © 2017 Journal of Guangdong University of Technology
Add：729 East Dongfeng RD., Guangzhou PRC. Postcode: 510090
Tel：020-37626653,020-37626139,020-37626396
Email：xbzrb@gdut.edu.cn
Supported:Beijing Magtech