Preparation of Nanosheet Al(OH)3/Mg(OH)2 Composite Retardant Coated with Oleic Acid

Huang Jian-zhi 1,2, Cheng Xiao-ling2   

  1. 1. School of Chemistry and Chemical Engineering, South China University of Technology, Guangzhou 510641, China; 2. School of Chemical Engineering and Light Industry, Guangdong University of Technology, Guangzhou 510006, China
  • Received:2015-04-22 Online:2016-03-23 Published:2016-03-23

HTML

PDF (PC)

2949

Abstract:

The nanosheet Al(OH)3/Mg(OH)2 composite retardant coated with oleic acid is synthesized through chemical compounding technique. The SEM result indicates that through changing the ratio of aluminum and magnesium can different morphology nanosheet composite retardant be prepared. The XRD result indicates that composite retardant is based on Al(OH)3, whose surface is coated with Mg(OH)2. The IR result indicates that composite retardant is coated with oleic acid by way of carboxylic acid salt. The EDS and TG result indicates that oleic acid is coated well-distributed, while Al(OH)3 and Mg(OH)2 are compounded near the ratio of reactant. The thermal analysis (TG and DTA) result indicates that compared with Al(OH)3, Mg(OH)2, and the physical mixture of Al(OH)3 and Mg(OH)2, flame retardancy of composite retardant is greatly improved.

Key words: composite flame retardant; aluminum hydroxide; magnesium hydroxide;  nanosheet; chemical compound; oleic acid

No related articles found!
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
Copyright © 2017 Journal of Guangdong University of Technology
Add：729 East Dongfeng RD., Guangzhou PRC. Postcode: 510090
Tel：020-37626653,020-37626139,020-37626396
Email：xbzrb@gdut.edu.cn
Supported:Beijing Magtech